silicon and 4-mercaptophenol

We report here plasma-induced formation of Ag nanostructures for surface-enhanced Raman scattering (SERS) applications. An array of uniform Ag patterned structures of 150 nm diameter was first fabricated on a silicon substrate with imprint lithography; then the substrate was further treated with an oxygen plasma to fracture the patterned structures into clusters of smaller, interconnected, closely packed Ag nanoparticles (20-60 nm) and redeposited Ag nanodots ( approximately 10 nm) between the clusters. The substrate thus formed had a uniform ultrahigh SERS enhancement factor (1010) over the entire substrate for 4-mercaptophenol molecules. By comparison, Au patterned structures fabricated with the same method did not undergo such a morphological change after the plasma treatment and showed no enhancement of Raman scattering.

Topics: Adsorption; Nanostructures; Oxygen; Particle Size; Phenols; Sensitivity and Specificity; Silicon; Silver; Spectrum Analysis, Raman; Sulfhydryl Compounds; Surface Properties