pectins and laponite

Bionanocomposite materials based on clays have been designed for oral administration and controlled release of a neuroprotective drug derivative of 5-methylindole, which had featured an innovative pharmacological mechanism for the treatment of neurodegenerative diseases such as Alzheimer's. This drug was adsorbed in the commercially available Laponite® XLG (Lap). X-ray diffractograms confirmed its intercalation in the interlayer region of the clay. The loaded drug was 62.3 meq/100 g Lap, close to the cation exchange capacity of Lap. Per se toxicity studies and neuroprotective experiments versus the neurotoxin okadaic acid, a potent and selective inhibitor of protein phosphatase 2A (PP2A), confirmed that the clay-intercalated drug did not exert toxicity in cell cultures and provided neuroprotection. Release tests of the hybrid material performed in media mimicking the gastrointestinal tract indicated a drug release in acid medium close to 25 %. The hybrid was encapsulated in a micro/nanocellulose matrix and processed as microbeads, with pectin coating for additional protection, to minimize release under acidic conditions. Alternatively, low density materials based on a microcellulose/pectin matrix were evaluated as orodispersible foams showing fast disintegration times, sufficient mechanical resistance for handling, and release profiles in simulated media that confirmed a controlled release of the encapsulated neuroprotective drug.

Topics: Administration, Oral; Cellulose; Clay; Delayed-Action Preparations; Drug Delivery Systems; Neuroprotective Agents; Pectins

In order to customize the viscoelastic properties of pectin gels, it is necessary to work on a composite platform. Herein, the gelation kinetics, and viscoelastic characterization of anionic polysaccharide pectin dispersion prepared in presence of nanoclay laponite are reported using dynamic light scattering and rheology measurements. The ratio Rg/Rh (Rg and Rh are radius of gyration and hydrodynamic radius respectively) determined from light scattering data revealed the presence of random coils of pectin chains inside the gel matrix. When nanoclay laponite was added to the pectin chains solution, two-phase separation was noticed instantaneously. Therefore, the surfactant cetyltrimethylammonium bromide [CTAB] was added to exfoliate the clay platelets in the dispersion, and also in its gel phase. The exfoliating agent cetyltrimethylammonium bromide ([CTAB]≈ cmc/10) helped to enhance the homogeneity and stability of the pectin-clay sols and gels. The storage and loss moduli (G' and G") of the composite gel changed significantly as function of nanoclay laponite content for concentration up to 0.03% (w/v) causing the softening of the gels (gel strength reduced by close to 50%) compared to pectin-calcium gel. However, as the concentration of nanoclay laponite was maintained between 0.01% and 0.03% (w/v), the gel rigidity (G') recovered by 30% (35-45 Pa). The transition from ergodic to non-ergodic state occurred during sol-gel transition owing to the presence of the nanoclay laponite. The gelation time was not too different from the ergodicity breaking time. Thus, the presence of nanoclay laponite in such minute concentration is shown to cause considerable change in the thermo-physical property of the composite gels. This material property modulation will facilitate designing of soft gels having storage modulus continuously varying in the wide range of 10-70 Pa while keeping the gelation temperature mostly unaltered.

Topics: Calcium; Cetrimonium; Cetrimonium Compounds; Elasticity; Hydrogels; Nanocomposites; Pectins; Rheology; Silicates; Viscosity; Water