The adherence of resin cements depends upon, among other factors, the polar interactions across the interface: resin cement/restorative material. The polar interactions may be augmented by inclusion of polar additives such as maleic anhydride to the cement monomer. However, maleic anhydride is slowly converted to maleic acid when exposed to an aqueous environment. This may affect mechanical properties of such a cement in a negative way. It was the aim of the present investigation to analyze the role of maleic anhydride dissolved in the monomer of resin cements. The resin cement monomers used were common methacrylates, to which maleic anhydride in amounts of up to 30 mol% was added. Polymerization initiators were included to make the materials dual curing. Finally, the preparations were mixed with silanated fillers. The adherence energy of the cements bonded to a chromium-cobalt alloy was assessed by means of the double cantilever beam test. The strength and stiffness of the resin cements were recorded at base line and after two months storage in water. The initial adherence energy increased by a factor of about two as a result of addition of maleic anhydride. However, resin cements containing maleic anhydride suffered significant reductions in long-term adherence, strength and stiffness. These reductions were particularly pronounced in non-irradiated specimens. The use of resin cements containing maleic anhydride is not a viable means of conveying adhesiveness to resin cements.

Topics: Adhesiveness; Adhesives; Aldehydes; Chemical Phenomena; Chemistry, Physical; Chromium Alloys; Composite Resins; Dental Bonding; Elasticity; Humans; Maleates; Maleic Anhydrides; Materials Testing; Methacrylates; Polyethylene Glycols; Polymers; Polymethacrylic Acids; Polyurethanes; Resin Cements; Silanes; Stress, Mechanical; Time Factors; Water